OLA PA11Pro is a high-performance nylon material made from castor oil, offering 100% bio-based environmental benefits. It provides exceptional ductility and impact resistance, making it ideal for mass production of strong, detailed parts across various industrial applications. Compared to PA12, PA11Pro is better suited for parts requiring flexibility and durability under dynamic stress.
Thermal Properties
Heat Deflection Temperature: 185 °C (0.45 MPa), 47 °C (1.82 MPa)
Mechanical Properties
Tensile Modulus (ASTM D638): 1.53 GPa
Tensile Strength (ASTM D638): 51 MPa
Elongation at Break (ASTM D638): 30%
Flexural Modulus (ASTM D790): 1.34 GPa
Flexural Strength (ASTM D790): 51 MPa
Notched Izod Impact Strength (ASTM D256): 7.4 J/m
Max. Part Size:
299mm × 199mm × 283mm
Tolerance and Precision：
±300 μm or ±0.3%