Titanium alloy TC4, also known as Ti6Al4V, is a medium-strength α-β phase titanium alloy with excellent mechanical properties, biocompatibility, and corrosion resistance. It is widely used in the aerospace, medical, and chemical industries.
As-Printed State
Surface roughness (sandblasted) ≥7μm
Hardness: HRC 38±3
Yield strength: 1050±50 MPa
Elongation: 7±3%
Tensile strength: 1230±50 MPa
Post-Heat Treatment
Hardness: HRC 35±3
Yield strength: 950±50 MPa
Elongation: 13±3%
Tensile strength: 1015±50 MPa
Key Notes
"As-printed" emphasizes the raw manufactured state.
"Post-heat treatment" replaces "heat-treated" for technical accuracy.
Units follow ISO/ASTM standards (e.g., MPa not Mpa).
Max. Part Size:
350mm x 400mm x 360mm
Tolerance and Precision：
±200μm or ±0.2%