This high-quality Ni-Cr alloy powder is specifically developed for dental 3D printing applications and complies with ISO 22674 standards.  The powder features sphericity of 0.86 and flowability of 29.3s/50g, ensuring smooth spreading and stable printing. Printed parts deliver a high-gloss finish after polishing, with yield strength of 754MPa, bending strength of 1300MPa, and elongation of 45.4% – combining high strength with excellent ductility. Metal-ceramic bond strength reaches 42.2MPa, with CTE well-matched to veneering porcelains for reliable bonding.  Suitable for crowns, bridges, and porcelain-fused-to-metal restorations. Available in three particle size ranges: 10~30μm, 10~45μm, and 15~53μm, with 5Kg standard packaging to meet diverse dental laboratory production needs.