This high-quality Co-Cr-W alloy powder is specifically developed for dental SLM（Selective Laser Melting）3D printing applications and complies with DIN EN ISO 22674 Type 5 standards.  The powder delivers exceptional mechanical properties – yield strength of 760MPa, ultimate tensile strength of 1090MPa, hardness of 425HV10, and metal-ceramic bond strength ≥25MPa, combined with good ductility and elastic modulus. The coefficient of thermal expansion（14.4×10⁻⁶K⁻¹）is well-matched with dental veneering porcelains, ensuring reliable metal-ceramic bonding.  Suitable for removable partial denture frameworks, clasps, and porcelain-fused-to-metal restorations. Available in three particle size ranges: 10~30μm, 15~45μm, and 15~53μm, with 5Kg standard packaging to meet diverse dental laboratory production needs.